Journalartikel

Jahr der Veröffentlichung: 2004

Seiten: 2948-2952

Zeitschrift: Chemistry of Materials

Bandnummer: 16

Heftnummer: 15

ISSN: 0897-4756

DOI Link: https://doi.org/10.1021/cm0495966

Verlag: American Chemical Society

Abstract: 
A strategy is shown to fabricate highly organized mesoporous anatase films exhibiting favorable properties for photocatalysis and photovoltaic applications by the hydrolysis/condensation of TiCl4 in the presence of PHB-PEO block copolymer templates. Dipcoating for evaporation-induced-self-assembly followed by a straight thermal treatment was employed. The evaporation/structuration process and the thermal treatment were mechanistically followed by in situ GISAXSIWAXS measurements, and the final product was carefully analyzed by spectroscopic ellipsometry and transmission electron microscopy to reveal the consequences of crystallization onto the micro-, the meso-, and the macroscale.

Harvard-Zitierstil: Smarsly, B., Grosso, D., Brezesinski, T., Pinna, N., Boissiere, C., Antonietti, M., et al. (2004) Highly crystalline cubic mesoporous TiO2 with 10-nm pore diameter made with a new block copolymer template, Chemistry of Materials, 16(15), pp. 2948-2952. https://doi.org/10.1021/cm0495966

APA-Zitierstil: Smarsly, B., Grosso, D., Brezesinski, T., Pinna, N., Boissiere, C., Antonietti, M., & Sanchez, C. (2004). Highly crystalline cubic mesoporous TiO2 with 10-nm pore diameter made with a new block copolymer template. Chemistry of Materials. 16(15), 2948-2952. https://doi.org/10.1021/cm0495966